FC422

AKSAD GROUP PETROCHEM

FC422

FC422 , is one of the TPC Performance expandable polystyrene products range. It is a free flowing expandable polystyrene grade,consisting of spherical polystyrene beads containing pentane as the expansion agent.

Expandable polystyrene (EPS) is normally expanded to achieve the low densities required for final step expansion.The typical density of this grade is around 25 kg/m3,but other densities are possible depending on applications and equipments.

FC422 is specially fast cycling and water proof formulated to achieve low density foam without lumps during pre-expansion.This grade is not fire retardent ,so it is not suitable for bulding applications

Applications:

High Density Block,Shape Molding

Because of its small bead size FC422 is also used for contour mouldings with a wall thickness of less than 10 mm.Moulding with greater wall thicknesses permit short cooling periods

Properly processed EPS foam packaging made from FC422 provides good mould filling properties and high mechanical strength.

It is not hygroscopic, and it does not become friable in low temperatures.

Moulded EPS packaging parts have to act as shock absorbers and cushion their content against blows from outside, i.e they have to absorb the energy released in an impact.

The mainly closed cell structure of moulded foam parts made from FC422 absorbs the impact stress as "deformation work".

In this process the air enclosed in the cells is first compressed, while bigger impact forces may also deform or crack the cell walls.

Packaging and storage:

FC422 is shipped in octabins (height 176 cm) on wooden pallets (115cm x 115 cm), containing 1000 kg net of material.

The octabins are not weather- or water-proof and must therefore not be exposed to outdoor conditions.

In order to obtain the desired properties of FC422, the raw material should be stored below 20 °C and be processed within 1 month.

Processing:

Preexpansion:

With discontinuously operating, state-of-the-art preexpanders FC422 can be preex-panded to densities of approx.25 kg/m3

Lower densities can be achieved by double preexpansion or in optimized machines.

FC422 has been treated with an antistatic agent to prevent a buildup of electro-static charge during transport. Intermediate aging:

Intermediate aging should be between 10 and 48 hours.

Moulding:

FC422 can be processed in industry standard moulding machines within a relatively wide range of steaming settings.

If a regenerative agent is added care has to be taken that the density of the regenerative agent equals the preexpansion density as closely as possible to prevent a segregation during production.

Typical Properties


 

TEST METHOD

TYPICAL VALUE

UNIT

PROPERTY

SUNPOR 7.2.5 (MIN 90% BY WT)

(0.5-0.7)(>90%wt)

MM

BEAD SIZE

SUNPOR 7.2.4

55

K-VALUE

SUNPOR 7.2.2

>5%

WT%

PENTANE CONTENT

SUNPOR 7.2.6

20-30

KG/M3

EXPANDED DENSITY

SUNPOR 7.2.1

500

PPM

RESIDUAL MONOMER

*All above mentioned data are typical values and not to be construed as real specifications.Users should confirm results by their own tests.For more information about guaranteed items, please refer to S.S.S.(Standard Sales Specifications)


 

 

 

 

 