1102XK

AKSAD GROUP PETROCHEM

1102 XK


POLYMER TYPE

POLYPROPYLENE HOMOPOLYMER

APPLICATION

Raffia, tape yarn, technical textiles, carpet backing, diary products

PRODUCT FEATURES

Homopolymer with low water carry over and preferred grade for tapes

PROCESSING METHOD

Extrusion

Properties

Test Method

Unit

Value

MFR ( 230˚ C/ 2.16 Kg )

ASTM D1238/L

gr/10min

4

Tensile Modulus of Elasticity (1mm/min)

ASTM D638

MPa

1500

Tensile Strength at Yield (50 mm/min)

ASTM D638

MPa

34

Elongation at Yield(50 mm/min)

ASTM D638

%

9

Notched Charpy Impact at 23˚

ISO 179/ 1eA

KJ/m2

4

Notched Charpy Impact at -30˚

ISO 179/ 1eA

KJ/m2

1.7

Vicat Softening Point, 10N

ASTM D1525

˚C

154

Ball indentation hardness

ISO 2039-1

MPa

74

HDT ( 0.46 N/mm2 )

ASTM D648

˚C

85

Melting Point , DSC

ASTM D3417

˚C

163

Density

ASTM D792

gr/cm3

0.91

The information in this publication is submitted without prejudice, and is based on our " .current knowledge and experience and on a limited number of tests In view of the many factors that may affect processing and application, these data do not relieve the receiver of this information from the Commercial 




Manager cell phone: +98- 912 127 45 75